[1][(4)__Full Text.......]
Discovered items are automatically translated into English so that you
can easily identify them.<br/><br/>If you would like to see them in
the original text, please use this button to switch between the two
options . Discoveries: ([2]Submit) English
Click to view (and print) basic analytics showing the makeup of
discovered items in this publication. [help.png]
[3][_] (83/ 256)
You can use the refine box to refine the discovered items in the
sections below.<br/>Simply type what you are looking for, any items
that do not match will be temporarily hidden. [4]____________________
[5][_]
Molecule
(34/ 107)
[6][_]
propylene
(28)
[7][_]
EVOH
(13)
[8][_]
ethylene
(11)
[9][_]
aluminium
(6)
[10][_]
ethylenealcohol
(5)
[11][_]
carbon
(4)
[12][_]
propylene-ethylene
(4)
[13][_]
XMNA
(4)
[14][_]
DES
(3)
[15][_]
vinyl ethylene-acetate
(3)
[16][_]
methyl ethylene-acrylate
(2)
[17][_]
butene-1
(2)
[18][_]
iron
(1)
[19][_]
hexene-1
(1)
[20][_]
acrylic acid
(1)
[21][_]
methacrylic acid
(1)
[22][_]
maleic acid
(1)
[23][_]
fumaric acid
(1)
[24][_]
itaconic acid
(1)
[25][_]
citraconic acid
(1)
[26][_]
mesaconic acid
(1)
[27][_]
maleic anhydride
(1)
[28][_]
citraconic anhydride
(1)
[29][_]
itaconic anhydride
(1)
[30][_]
8,9,10-octahydronaphthalene-2,2-dicarboxylic acid anhydride
(1)
[31][_]
maleopimaric acid
(1)
[32][_]
tetrahydrophthalic anhydride
(1)
[33][_]
methylnorbornyl-5-ene-2,3-dicarboxylic acid anhydride
(1)
[34][_]
norbornyl-5-ene-2,3-dicarboxylic acid anhydride
(1)
[35][_]
R-O-OH
(1)
[36][_]
t-butyl hydroperoxide
(1)
[37][_]
pinane hydroperoxide
(1)
[38][_]
cumene hydroperoxide
(1)
[39][_]
copper
(1)
[40][_]
Polymer
(7/ 59)
[41][_]
POLYETHYLENE
(28)
[42][_]
Nylon
(11)
[43][_]
Polypropylene
(8)
[44][_]
Polyvinyl Alcohol
(7)
[45][_]
Polyolefine
(3)
[46][_]
Polyesters
(1)
[47][_]
Cellophane
(1)
[48][_]
Generic
(13/ 37)
[49][_]
hydrocarbons
(7)
[50][_]
aliphatic
(5)
[51][_]
anhydride
(5)
[52][_]
metals
(4)
[53][_]
acids
(4)
[54][_]
carboxylic acids
(3)
[55][_]
ETHYLENic
(2)
[56][_]
hydroperoxide
(2)
[57][_]
1,2-anhydride
(1)
[58][_]
bicyclo anhydride
(1)
[59][_]
radical
(1)
[60][_]
methylbicyclo anhydride
(1)
[61][_]
acid anhydride
(1)
[62][_]
Physical
(20/ 36)
[63][_]
0 L
(6)
[64][_]
45 %
(4)
[65][_]
9 L
(4)
[66][_]
5 s
(3)
[67][_]
2 s
(2)
[68][_]
10 %
(2)
[69][_]
100 %
(2)
[70][_]
1 minute
(1)
[71][_]
20 minutes
(1)
[72][_]
10 min
(1)
[73][_]
127-178 gm
(1)
[74][_]
de 25,4 mm
(1)
[75][_]
de 1,4 kg/cm
(1)
[76][_]
de 0,66 kg/cm
(1)
[77][_]
de 0,59 kg/cm
(1)
[78][_]
8 g/cm
(1)
[79][_]
3 l
(1)
[80][_]
999 %
(1)
[81][_]
30-0,001 %
(1)
[82][_]
25-90 %
(1)
[83][_]
Gene Or Protein
(4/ 11)
[84][_]
Etre
(8)
[85][_]
DANS
(1)
[86][_]
Adhe
(1)
[87][_]
Hsd
(1)
[88][_]
Substituent
(5/ 6)
[89][_]
heptyl
(2)
[90][_]
4-methyl-cyclohexyl
(1)
[91][_]
octyl
(1)
[92][_]
nonyl
(1)
[93][_]
methyl
(1)
Export to file:
Export Document and discoveries to Excel
Export Document and discoveries to PDF
Images Mosaic View
Publication
_________________________________________________________________
Number FR2517689A1
Family ID 1901693
Probable Assignee Enron Chemical Co
Publication Year 1983
Title
_________________________________________________________________
FR Title MELANGES ADHESIFS ET STRUCTURES COMPOSITES
Abstract
_________________________________________________________________
L'INVENTION CONCERNE UN MELANGE ADHESIF AYANT UNE BONNE ADHESION
VIS-A-VIS DE DIFFERENTS SUBSTRATS, ET COMPRENANT DES MELANGES D'UN
TRONC DE POLYETHYLENE SUR LEQUEL SONT GREFFES DES carboxylic acids
MONOMERES POLYMERISABLES A INSATURATION ETHYLENic, ET CONTENANT EN
OUTRE UNE RESINE DE MELANGE FORMEE DE POLYETHYLENES HAUTE DENSITE ET
DE POLYPROPYLENES.
L'INVENTION TROUVE SON APPLICATION PRINCIPALE DANS L'INDUSTRIE DES
ADHESIFS.
Description
_________________________________________________________________
L'invention concerne des melanges adhesifs et des
structures composites.
Les adhesifs extrudables a base de polyethylene haute densite (PEHD)
presentent un grand interet; en effet, ils presentent de meilleures
proprietes de resistance aux hau-
tes temperatures et de barriere anti-humidite que les adhe-
sifs a base de polyethylene basse densite (PEBD), de poly-
ethylene basse densite lineaire (PEBDL), d'vinyl ethylene-acetate
(EVA), d'methyl ethylene-acrylate (EMA) ou d'autres copolymeres de
l'ethylene Pour une raison ou une autre, qui n'est pas completement
elucidee, les adhesifs a
base de PEHD presentent une adhesion vis-a-vis des poly-
meres polaires plus faible que ceux bases sur les autres
polymeres polyethyleniques tels que decrits ci-dessus.
Pour ameliorer l'adherence des adhesifs a base de
PEHD, on a ajoute a leur composition des materiaux elasto-
meres Cette solution n'est pas toujours satisfaisante, car
l'elastomere abaisse habituellement d'une maniere conside-
rable le point de ramollissement et l'indice de fusion, tout en
influant sur les caracteristiques de rigidite et de
barriere anti-humidite de la composition consideree.
Par melange de quantites appropriees de poly-
propylene, de PEHD et d'un copolymere polyethylenique gref-
fe, on a pu obtenir des adhesifs presentant une excellente adhesion
vis-avis des polymeres polaires comme le "Nylon",
des copolymeres ethylenealcohol vinylique (EVOH), des poly-
meres et copolymeres de l'polyvinyl alcohol, des metals, du verre, du
papier, du bois, etc Ces composites, qui forment l'objet de
l'invention, peuvent etre prepares par toute methode connue des
specialistes On peut citer a
titre d'exemple la stratification, la coextrusion, l'enduc-
tion par coextrusion et une combinaison de ces methodes, ou toute
autre methode destinee a assembler des materiaux dissemblables et
connue des specialistes La raison pour laquelle l'addition de
polypropylene a ces melanges ameliore
l'adhesion n'est pas parfaitement comprise.
Le terme "polyethylene", tel qu'utilise dans la pre-
sente description pour le tronc de greffage, englobe les
homopolymeres de l'ethylene et les copolymeres de l'ethy-
lene et du propylene, du butene-1 et d'autres hydrocarbons aliphatic
insatures, de preference ayant jusqu'a 8 atomes de carbon De
preference, le polymere de l'ethylene
est lineaire De meme, on prefere, de temps a autre, gref-
iron des melanges de deux des homopolymeres et copolymeres,
ou plus Les homopolymeres polyethyleniques et les copoly-
meres de l'ethylene peuvent etre prepares par tout procede connu, par
l'utilisation de catalyseurs aux metals de
transition, sous pression faible ou moyenne, ou des initia-
teurs radicalaires sous haute pression En consequence, les polymeres
peuvent etre des polyethylenes basse densite, des polyethylenes
moyenne densite ou des polyethylenes haute
densite.
L'expression "polymeres polyethylaniques haute densite"
utilisee dans la presente description pour designer une
resine de melange englobe les homopolymeres de l'ethylene et les
copolymeres de l'ethylene et du propylene, du
butene-1, de l'hexene-1 et d'autres hydrocarbons aliphati-
ques insatures, dont le nombre d'atomes de carbon est de
preference inferieur ou egal a 8 Il est quelquefois prefe-
rable d'utiliser dans la resine de melange des melanges de
deux des homopolymeres ou copolymeres ci-dessus, ou plus.
De preference, ce polyethylene haute densite a une densite
d'environ 0,94-0,97.
Le polypropylene de la resine de melange comprend les homopolymeres du
propylene et les copolymeres du propylene et d'un ou plusieurs
hydrocarbons aliphatic insatures,
ayant de preference jusqu'a 8 atomes de carbon.
Alors que les polymeres ci-dessus representent des formes de
realisation preferees de l'invention, ils ne
doivent pas etre consideres comme en limitant le cadre.
Les carboxylic acids insatures ou derives d'acidsutilises en tant que
monomeres de greffage englobent des composes tels que l'acrylic acid,
l'methacrylic acid, l'maleic acid, l'fumaric acid, l'itaconic acid,
l'citraconic acid, l'mesaconic acid, l'maleic anhydride, l'citraconic
anhydride, l'itaconic anhydride,
l'acid4-methyl-cyclohexyl-4-ene-1,2-anhydride-
dicarboxylique, l'acidbicyclo anhydride( 2 2 1)octyl-
5-ene-2,3-dicarboxylique, l'anhydride de l'acide
1,2,3,4,,8,9,10-octahydronaphthalene-2,2-dicarboxylic acid anhydride,
le 2-oxa- 1,3-dicetospiro( 4,4) nonyl-7-ene, l'anhydridebicyclo( 2 o 2
1) heptyl-5-ene-2,3dicarboxylique, l'maleopimaric acid,
l'tetrahydrophthalic anhydride, l'anhydride de l'acide
x-methylnorbornyl-5-ene-2,3-dicarboxylic acid anhydride,
l'norbornyl-5-ene-2,3-dicarboxylic acid anhydride, l'anhydrideNadic,
l'anhydridemethyl-Nadic, l'anhydrideHimic, l'anhydridemethylHimic et
d'autres monomeres a noyaux
condenses decrits dans les brevets des Etats-Unis d'Ameri-
que N 3 873 643 et 3 882 194 On peut aussi utiliser dans le cadre de
l'invention des copolymeres cogreffes tels que decrits dans le brevet
des Etats-Unis N 3 882 194 Le procede de preparation des copolymeres
greffes est decrit
dans les brevets des Etats-Unis d'Amerique ci-dessus.
Il est quelquefois souhaitable d'utiliser plusieurs
monomeres de greffage, pour jouer sur les proprietes physi-
ques des produits finis En regle generale, le procede consiste a
chauffer un melange du ou des polymeres et du ou des monomeres, avec
ou sans solvant On peut chauffer le melange au-dessus du point de
fusion de la polyolefine, avec ou sans catalyseur Ainsi, le greffage
se produit en presence d'air, d'hydroperoxydes, d'autres catalyseurs
de radicaux libres ou, de preference, essentiellement en
l'absence des produits pour lesquels le melange est main-
tenu a des temperatures elevees et (si l'on n'utilise pas de solvant),
de preference sous une forte contrainte de cisaillement. Les
copolymeres greffes et cogreffes utilises dans le cadre de l'invention
sont recuperes par tout procede ou
systeme qui separe ou utilise le copolymere greffe produit.
Ainsi, cette expression englobe la recuperation du copo-
lymere sous la forme de flocons precipites, de pastilles, de poudres,
etc, de meme que les pastilles, poudres, etc, melangees ou ayant subi
une reaction chimique, ou encore sous la forme d'articles formes
directement a
partir du copolymere obtenu.
On peut utiliser dans le procede selon l'invention n'importe lequel
des hydroperoxydes connus presentant une periode de demi-vie d'au
moins 1 minute a 145 'C Ces hydroperoxydes presentent la formule
generale R-O-OH, o
R est un radical organique Parmi les hydroperoxydes con-
venables, on peut citer l't-butyl hydroperoxide, l'hydroperoxyde de
pmenthanhydroperoxide, l'
pinane hydroperoxide
et l'cumene hydroperoxide, ainsi que d'autres hydro-
peroxydes connus La temperature elevee conduit a une rapide
decomposition de l'hydroperoxide, ce qui catalyse la reac-
tion entre la polyolefine et le monomere pour donner le
copolymere greffe.
Bien evidemment, plus le melange sera homogene avant le chauffage, et
moins il sera necessaire de melanger la
solution ou la composition fondue Generalement, pour obte-
nir un taux de conversion donne, on a constate qu'il etait tres
souhaitable de proceder a une certaine forme de melange en presence
d'un solvant, meme s'il se forme avant le chauffage un melange
uniforme de tous les constituants de la composition En general, quand
aucun solvant n'est
utilise, la composition doit etre chauffee a une tempera-
ture superieure a environ 130 'C, et, de preference, on utilisera des
temperatures comprises entre environ 200 et
450 OC.
Il faut generalement eviter des temperatures tres superieures a
environ 4500 C, pour eviter le risque d'une
trop forte decomposition des constituants polymeres Cepen-
dant, si les produits de decomposition ne sont pas souhai-
tes dans le produit, comme par exemple lors de la production des cires
presentant un indice de fusion eleve, on peut faire appel a des
temperatures plus elevees Le temps de reaction necessaire est tres
court, et il est de l'ordre de quelques secondes aenviron 20 minutes,
bien que des durees
17689
de chauffage plus longues n'affectent pas le produit d'une maniere
considerable et puissent etre utilisees si, pour
une raison ou une autre, on le souhaite.
Un procede commode de mise en oeuvre de la reaction consiste a
premelanger les ingredients puis a extruder la composition dans une
extrudeuse chauffee On peut aussi utiliser dans le procede d'autres
moyens de melangeage, comme un melangeur Brabender, un melangeur
Banbury, un
malaxeur a rouleaux, etc Pour eviter une augmenta-
tion exageree de la masse moleculaire, avec un risque de reticulation
aux temperatures elevees, il est souhaitable de conduire la reaction
dans un recipient ferme On peut obtenir ce resultat a l'aide d'une
extrudeuse a vis simple ou multiple, sans qu'il soit necessaire de
faire appel a des equipements auxiliaires, et c'est la raison pour
laquelle ce type d'extrudeuse est un reacteur particuliere-
ment souhaite.
Les adhesifs selon l'invention peuvent etre utilises dans des
composites contenant des substrats polaires comme le "Nylon", les
copolymeres ethylenealcohol vinylique (EVOH),
l'polyvinyl alcohol (polyvinyl alcohol), des polyesters, du poly-
urethanne, des metals, etc Ces compositions peuvent etre formees de
juste deux couches, ou bien elles peuvent former trois couches, ou
plus, en ajoutant a la structure des materiaux adherant a l'une des
couches Par exemple, on peut utiliser dans ces couches des
polyolefines du type polyethylene (polyethylene), des copolymeres
vinyl ethylene-acetate (EVA) ou des copolymeres de l'ethylene et
d'autres monomeres et du propylene (propylene) Il est evident que les
specialistes pourront preparer de nombreuses combinaisons en utilisant
les principes presentes dans la presente invention. Voici des exemples
de composites selon l'invention: adhesif/"Nylon",adhesif/aluminium,
adhesif/EVOH, propylene/adhesif/ "Nylon",
polyethylene/adhesif/"Nylon': EVA/adhesif/polyvinyl alcohol,
propylene/adhesif/polyvinyl alcohol, EVA/adhesif/EVOH,
propylene/adhesif/aluminium, polyethylene/adhesif/aluminium,
polyethylene/adhesif/EVOH, propylene/adhesif/EVOH,
EVA/adhesif/aluminium, polyethylene/adhesif/acier,
propylene/adhesif/copper, EVA/adhesif/verre,
propylene/adhesif/bois, polyethylene/adhesif/polyurethanne On peut
prepa-
rer des structures a quatre et cinq couches, ou plus,
comprenant les couches ci-dessus A titre d'exemples seule-
ment, on peut preparer des structures multicouches, par exemple les
structures suivantes: propylene/adhesif/"'Nylon"/ adhesif/EVA,
propylene/adhesif/EVOH/adhesif/polyethylene,
polyethylene/adhesif/"Nylon"/ adhesif/propylene,
polyethylene/adhesif/aluminium/adhesif/EVA Le mot
"adhesif" s'entend pour un melange adhesif selon l'inven-
tion Les composites ci-dessus ne sont presentes qu'a titre d'exemples
Il est evident que les specialistes pourront
preparer de nombreuses autres structures.
Lors de la preparation des composites, on peut utili-
ser tout moyen destine a assembler deux couches, ou plus, connus des
specialistes Les procedes connus sont la
coextrusion des films par soufflage, la coextrusion film-
feuille par coulee, la coextrusion par moulage par souf-
flage, la stratification et l'enduction par coextrusion.
Les autres procedes sont l'enduction par poudrage, le rotomoulage, la
coextrusion de profiles, la coextrusion pour l'enduction de fils
metalliques, etc. On peut utiliser tout equipement ou technique de
melangeage pour preparer des melanges selon l'invention a
partir des copolymeres greffes, homopolymeres et copoly-
meres du propylene et de l'ethylene ci-dessus A titre d'exemple, on
peut preparer des melanges dans une tete de melangeage Plasticorder
Brabender a chauffage electrique,
en utilisant un melangeur a vis dans les conditions sui-
vantes: temperature 204,4 C, vitesse du rotor 120 t/min, duree du
melangeage 10 min apres fusion Les melanges obtenus ont subi un
moulage par compression pour donner des films d'epaisseur
approximative 127-178 gm Les films ont ete ensuite thermoscelles sur
le substrat faisant l'objet de l'evaluation, a une temperature et
pendant un temps appropries Ces conditions sont les suivantes:
1."Nylon" 6: 221,1 C, 2 s.
2 Copolymere ethylenealcohol vinylique (EVOH):
221,1 C, 5 s.
3 Polypropylene: 260 C, 5 s.
4 Aluminium: 221,1 C, 2 s.
On a fait subir des essais aux composites obtenus, en les decoupant en
des bandes de 25,4 mm de large On a aussi determine l'adhesion par
l'essai d'ecaillage a
l'eprouvette angulaire selon ASTM D 187-72.
Exemple,
On a prepare un melange contenant 45 % d'un copolymere
sequence propylene-ethylene presentant un indice de flui-
dite de 2 et une densite de 0,90, 45 % d'un polyethylene haute densite
(PEHD) ayant un indice de fusion de 2,7 et une densite de 0,958, et 10
% d'un PEHD auquel on avait greffe XMNA On a thermoscelle un film de
ce materiau sur un film d'un copolymere ethylenealcohol vinylique
pendant S a 221,1 C L'adhesion a l'essai d'ecaillage a l'eprou-
vette angulaire a ete de 1,4 kg/cm.
Exemple 2
On a thermoscelle le meme melange que celui utilise dans l'Exemple 1
sur du "Nylon" 6 pendant 2 S a 221,1 C On observe une adhesion a
l'essai d'ecaillage a l'eprouvette
angulaire de 0,66 kg/cm.
Exemple 3
On a prepare un melange contenant 45 % d'un copolymere
sequence propylene-ethylene presentant un indice de flui-
dite de 4 et une densite de 0,90, 45 % d'un PEHD ayant une densite de
0, 96 et un indice de fusion de 0,8, et 10 % d'un PEHD sur lequel on
avait greffe du XMNA L'adhesion vis-a-vis du EVOH est de 0,59 kg/cm
dans les conditions
d'essai de l'Exemple 1.
Exemples 4-10
On a prepare et thermoscelle sur du EVOH pendant 5 s a 221,1 C des
melanges d'un PEHD ayant une densite de 0,96 et un indice de fusion de
0, 8 g/cm, d'un copolymere sequence propylene-ethylene ayant un indice
de fluidite de 2,0 et une densite de 0,90, et d'un PEHD sur lequel on
avait greffe du XMNA Les resultats sont presentes sur le
Tableau I On peut obtenir une excellente adherence vis-4-
vis du EVOH dans le cas des melanges contenant du PEHD et du
propylene, si on les compare aux melanges ne contenant que du PEHD. On
a thermoscelle sur un polypropylene statistique
(propylene) pendant 5 S a 2600 C les melanges decrits ci-dessus.
Le Tableau I presente l'adhesion a l'essai d'ecaillage
sur eprouvette angulaire de ces echantillons On peut obte-
nir une excellente adherence vis-a-vis du propylene pour les melanges
contenant du PEHD et du propylene, si on les compare aux
melanges ne contenant que du PEHD.
Exemples 11-17
On a prepare des melanges en utilisant le PEHD, le copolymere sequence
propylene-ethylene et le copolymere greffe decrits dans l'Exemple 4
Les melanges ont ete thermoscelles pendant 2 S sur du "Nylon" 6 a
221,1 OC Les resultats des essais d'adherence sont presentes sur le
Tableau II On voit que l'on peut obtenir une excellente adherence
vis-a-vis du "Nylon" 6 si l'on utilise des melanges dans lesquels on
ajoute du propylene a un melange de PEHD et d'un
copolymere greffe.
TABLEAU I
Composition p P Copolymere greffe
10
47,5 Adhesion EVOH kg/cm 0,0 0,18 0,52
0,98 F
1 4 0,98 1 4 pp kg/cm 0,05 0,04 0,21 0, 36 0,55 1,27
0,88 F
F = dechirement du film adhesif -.b Co
Exemple
PEHD 47,, O. Co %O r- qt-, Ln cm a,e OT'1 x" ep MIT; n p quemea Tqogp
= IN
EL', O
E.z 1 O t E 1 O ct,,, O
IN OLIO
IN zq', O 9 L Io ul D/b 3 l '9 IA E IN-01 np s TA-iq-s TA uo Tsptlpv 0
L 0 L 0 L 0 L 0 L 0 L OL. pije xb eaqul KT Od OD 99 Sz
99 SE
Sp Sp
SE: 99
Sz 99
9 L cu
ci ci a Hsd UOT 4 T Soduio D L L 9 L 9 L t, L E L z L L L G Td UIOXE 1
C) 1 v- il rivarlavl 1 1 Glossaire des abreviations EMA = methyl
ethylene-acrylate EVA = copolymere vinyl ethylene-acetate EVOH =
copolymere ethylenealcohol vinylique PEHD = polyethylene haute
densite, de preference avec
une densite de 0,94-0,97.
PEBD = polyethylene basse densite PEBDL = polyethylene basse densite
lineaire polyethylene = polyethylene propylene = polypropylene:
homopolymeres du propylene et copolymeres du propylene et d'un ou
plusieurs hydrocarbons aliphatic insatures ayant de preference un
nombre
d'atomes de carbon inferieur ou egal a 8.
polyvinyl alcohol = polyvinyl alcohol XMNA = acidx-methylbicyclo
anhydride( 2 2 1) heptyl-5-ene-2,3-dicarboxylique.
Bien entendu, l'invention n'est pas limitee aux exem-
ples de realisation ci-dessus decrits et representes, a partir
desquels on pourra prevoir d'autres modes et d'autres formes de
realisation, sans pour cela sortir du
cadre de l'invention.
Claims
_________________________________________________________________
Revendications
1 Melange adhesif, caracterise en ce qu'il comprend (a) environ 0,1-40
parties en poids, dans le melange, d'un copolymere greffe forme de
70-99, 999 % en poids d'un tronc de polyethylene sur lequel sont
greffes environ 30-0,001 % en poids d'au moins un monomere de greffage
comprenant au moins un carboxylic acid a insaturation ethylenic
polymerisable, ou un acid anhydride carboxylique, le total faisant 100
% et (b) environ 99,9-60 parties en poids d'une resine mixte de
melange formee d'environ 25-90 % en poids d'un polyethylene haute
densite et d'environ 75- % en poids d'un polypropylene, le total
faisant 100 %.
2 Melange selon la revendication 1, caracterise en ce que le
polypropylene englobe les homopolymeres du propy- lene et les
copolymeres du propylene et d'un ou plusieurs hydrocarbons aliphatic
insatures.
3 Melange selon la revendication 1, caracterise en ce que la resine
mixte composee de polyethylene haute densite comprend des
homopolymeres de l'ethylene et des copolymeres de l'ethylene et d'un
hydrocarbon insature.
4 Structure composite, caracterisee en ce qu'elle -est constituee (a)
d'un substrat et, colle a ce dernier, (b) d'un melange adhesif selon
la revendication 1.
5 Structure composite selon la revendication 4, caracterisee en ce que
le substrat est forme de polymeres polaires, de metals solides, de
verre, de papier, de bois ou de cellophane.
6 Structure composite, caracterisee en ce qu'elle est constituee (a)
de deux substrats, ou plus, avec des ele- ments apparies adjacents
colles l'un a l'autre par (b) une couche intercalaire du melange
adhesif selon la revendica- tion 1 X
7 Structure composite selon la revendication 6, caracterisee en ce que
(a) est compose de polypropylene et d'un substrat polaire.
8 Structure composite selon la revendication 6, caracterisee en ce que
(a) se compose de substrats polaires.
9 Structure composite selon la revendication 4, caracterisee en ce que
le substrat est compose d'homopoly- meres du propylene et de
copolymeres du propylene et d'un ou plusieurs hydrocarbons aliphatic
insatures.
10 Procede de preparation d'une structure composite selon la
revendication 4, caracterise en ce que l'on fait adherer les
constituants les uns aux autres par des proce- des englobant la
coextrusion d'un film par soufflage, la coextrusion d'un film par
coulee, la coextrusion par moulage par soufflage, la stratification,
l'enduction par extrusion ou coextrusion, l'enduction par poudrage, le
rotomoulage, la coextrusion de profiles ou l'extrusion ou la
coextrusion par enduction de fils metalliques.
? ?
Display vertical position markers.<br/><br/>This option will display
the relative positions of currently selected key terms within the full
document length.<br/><br/>You can then click the markers to jump to
general locations within the document, or to specific discoveries if
you know whereabouts in the document they occur. [96][_]
Open a preview window.<br/><br/>This window will provide a preview of
any discovery (or vertical marker) when you mouse over
it.<br/><br/>The preview window is draggable so you may place it
wherever you like on the page. [97][_]
[static.png]
[close.png]
Discovery Preview
(Mouse over discovery items)
[textmine.svg] textmine Discovery
« Previous
Multiple Definitions ()
Next »
Enlarge Image (BUTTON) ChemSpider (BUTTON) PubChem (BUTTON) Close
(BUTTON) X
(BUTTON) Close
(BUTTON) X
TextMine: Publication Composition
FR2517689
(BUTTON) Print/ Download (BUTTON) Close
1. Welcome to TextMine.
The TextMine service has been carefully designed to help you
investigate, understand, assess and make discoveries within patent
publications, quickly, easily and efficiently.
This tour will quickly guide you through the main features.
Please use the "Next" button in each case to move to the next step
of the tour (or you can use [Esc] to quit early if you don't want
to finish the tour).
2. The main menu (on the left) contains features that will help you
delve into the patent and better understand the publication.
The main feature being the list of found items (seperated into
colour coded categories).
3. Click the Minesoft logo at any time to reset TextMine to it's
initial (start) state.
4. You can select which part of the document you'd like to view by
using the pull down menu here.
You can select "Full Text" to view the entire document.
5. For non-latin languages, (in most cases) full text translations
are available, you can toggle them on and off here.
You can also toggle the inline discovery translations between
English and their original language.
6. The pie chart icon will open a basic statistical breakdown of the
publication.
7. The sort icon allows you to sort the listed categories based on
the number of instances found.
Click to toggle between ascending and descending.
8. You can use the refine box to refine the discovered items in the
sections below.
Simply type what you are looking for, any items that do not match
will be temporarily hidden.
9. The publication has been analysed and we have identified items
within it that fit into these categories.
The specific items found are listed within the category headings.
Click the section header to open that section and view all the
identitfied items in that section.
If you click the checkbox all items in that section will be
highlighted in the publication (to the right).
The best thing to do is to experiment by opening the sections and
selecting and unselecting checkboxes.
10. The main output window contains the publication full text (or part
thereof if selected).
11. The Tools section contains tools to help you navigate the
"discovered" (highlighted) items of interest.
The arrows and counter let you move through the highlighted items
in order.
12. Other tools include a "Preview" option [ [preview.png] ] and the
ability to mark the relative locations of highlighted items by
using the "Marker" option [ [marker.png] ].
Try these out to best understand how they work, and to discover if
they are of use to you.
13. Items selected from the menu on the left will be highlighted in
the main publication section (here in the middle of the screen).
Click them for further information and insights (including
chemical structure diagrams where available).
14. Please experiment with TextMine - you cannot make any permanent
changes or break anything and once your session is closed (you've
log out) all your activity is destroyed.
Please contact Minesoft Customer Support if you have any questions
or queries at: [email protected]
[98]____________________
[99]____________________
[100]____________________
[101]____________________
[102]____________________
[103]____________________
[104]____________________
[105]____________________
[106]____________________
[107]____________________
[BUTTON Input] (not implemented)_____ [BUTTON Input] (not
implemented)_____
Документ
Категория
Без категории
Просмотров
1
Размер файла
31 Кб
Теги
fr2517689a1
1/--страниц
Пожаловаться на содержимое документа